AISI 301L Stainless Steel vs. AISI 316 Stainless Steel
Both AISI 301L stainless steel and AISI 316 stainless steel are iron alloys. They have a moderately high 92% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is AISI 301L stainless steel and the bottom bar is AISI 316 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 210 to 320 | |
| 160 to 360 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Elongation at Break, % | 22 to 50 | |
| 8.0 to 55 |
| Fatigue Strength, MPa | 240 to 530 | |
| 210 to 430 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 77 | |
| 78 |
| Shear Strength, MPa | 440 to 660 | |
| 350 to 690 |
| Tensile Strength: Ultimate (UTS), MPa | 620 to 1040 | |
| 520 to 1180 |
| Tensile Strength: Yield (Proof), MPa | 250 to 790 | |
| 230 to 850 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 290 |
| Maximum Temperature: Corrosion, °C | 410 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 890 | |
| 590 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1400 |
| Melting Onset (Solidus), °C | 1390 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 15 | |
| 15 |
| Thermal Expansion, µm/m-K | 16 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.3 | |
| 2.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 2.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 13 | |
| 19 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 3.9 |
| Embodied Energy, MJ/kg | 39 | |
| 53 |
| Embodied Water, L/kg | 130 | |
| 150 |
Common Calculations
| PREN (Pitting Resistance) | 19 | |
| 26 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 210 to 300 | |
| 85 to 260 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 160 to 1580 | |
| 130 to 1820 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 22 to 37 | |
| 18 to 41 |
| Strength to Weight: Bending, points | 21 to 29 | |
| 18 to 31 |
| Thermal Diffusivity, mm2/s | 4.1 | |
| 4.1 |
| Thermal Shock Resistance, points | 14 to 24 | |
| 11 to 26 |
Alloy Composition
| Carbon (C), % | 0 to 0.030 | |
| 0 to 0.080 |
| Chromium (Cr), % | 16 to 18 | |
| 16 to 18 |
| Iron (Fe), % | 70.7 to 78 | |
| 62 to 72 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0 | |
| 2.0 to 3.0 |
| Nickel (Ni), % | 6.0 to 8.0 | |
| 10 to 14 |
| Nitrogen (N), % | 0 to 0.2 | |
| 0 to 0.1 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.75 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |