AISI 301L Stainless Steel vs. EN 1.7383 Steel
Both AISI 301L stainless steel and EN 1.7383 steel are iron alloys. They have 78% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is AISI 301L stainless steel and the bottom bar is EN 1.7383 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 210 to 320 | |
| 170 to 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 22 to 50 | |
| 20 to 23 |
| Fatigue Strength, MPa | 240 to 530 | |
| 210 to 270 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 74 |
| Shear Strength, MPa | 440 to 660 | |
| 350 to 380 |
| Tensile Strength: Ultimate (UTS), MPa | 620 to 1040 | |
| 560 to 610 |
| Tensile Strength: Yield (Proof), MPa | 250 to 790 | |
| 300 to 400 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 890 | |
| 460 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1470 |
| Melting Onset (Solidus), °C | 1390 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 15 | |
| 39 |
| Thermal Expansion, µm/m-K | 16 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.3 | |
| 7.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 8.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 13 | |
| 3.9 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 1.8 |
| Embodied Energy, MJ/kg | 39 | |
| 23 |
| Embodied Water, L/kg | 130 | |
| 59 |
Common Calculations
| PREN (Pitting Resistance) | 19 | |
| 5.6 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 210 to 300 | |
| 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 160 to 1580 | |
| 240 to 420 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 22 to 37 | |
| 20 to 22 |
| Strength to Weight: Bending, points | 21 to 29 | |
| 19 to 20 |
| Thermal Diffusivity, mm2/s | 4.1 | |
| 11 |
| Thermal Shock Resistance, points | 14 to 24 | |
| 16 to 18 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.040 |
| Carbon (C), % | 0 to 0.030 | |
| 0.080 to 0.15 |
| Chromium (Cr), % | 16 to 18 | |
| 2.0 to 2.5 |
| Copper (Cu), % | 0 | |
| 0 to 0.3 |
| Iron (Fe), % | 70.7 to 78 | |
| 94.3 to 96.6 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0.4 to 0.8 |
| Molybdenum (Mo), % | 0 | |
| 0.9 to 1.1 |
| Nickel (Ni), % | 6.0 to 8.0 | |
| 0 to 0.3 |
| Nitrogen (N), % | 0 to 0.2 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.010 |