AISI 301L Stainless Steel vs. Grade 20 Titanium
AISI 301L stainless steel belongs to the iron alloys classification, while grade 20 titanium belongs to the titanium alloys. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is AISI 301L stainless steel and the bottom bar is grade 20 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 120 |
| Elongation at Break, % | 22 to 50 | |
| 5.7 to 17 |
| Fatigue Strength, MPa | 240 to 530 | |
| 550 to 630 |
| Poisson's Ratio | 0.28 | |
| 0.32 |
| Shear Modulus, GPa | 77 | |
| 47 |
| Shear Strength, MPa | 440 to 660 | |
| 560 to 740 |
| Tensile Strength: Ultimate (UTS), MPa | 620 to 1040 | |
| 900 to 1270 |
| Tensile Strength: Yield (Proof), MPa | 250 to 790 | |
| 850 to 1190 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 890 | |
| 370 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1660 |
| Melting Onset (Solidus), °C | 1390 | |
| 1600 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 520 |
| Thermal Expansion, µm/m-K | 16 | |
| 9.6 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 5.0 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 52 |
| Embodied Energy, MJ/kg | 39 | |
| 860 |
| Embodied Water, L/kg | 130 | |
| 350 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 210 to 300 | |
| 71 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 160 to 1580 | |
| 2940 to 5760 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 33 |
| Strength to Weight: Axial, points | 22 to 37 | |
| 50 to 70 |
| Strength to Weight: Bending, points | 21 to 29 | |
| 41 to 52 |
| Thermal Shock Resistance, points | 14 to 24 | |
| 55 to 77 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 3.0 to 4.0 |
| Carbon (C), % | 0 to 0.030 | |
| 0 to 0.050 |
| Chromium (Cr), % | 16 to 18 | |
| 5.5 to 6.5 |
| Hydrogen (H), % | 0 | |
| 0 to 0.020 |
| Iron (Fe), % | 70.7 to 78 | |
| 0 to 0.3 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 |
| Molybdenum (Mo), % | 0 | |
| 3.5 to 4.5 |
| Nickel (Ni), % | 6.0 to 8.0 | |
| 0 |
| Nitrogen (N), % | 0 to 0.2 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.12 |
| Palladium (Pd), % | 0 | |
| 0.040 to 0.080 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 71 to 77 |
| Vanadium (V), % | 0 | |
| 7.5 to 8.5 |
| Zirconium (Zr), % | 0 | |
| 3.5 to 4.5 |
| Residuals, % | 0 | |
| 0 to 0.4 |