AISI 301LN Stainless Steel vs. 6101B Aluminum
AISI 301LN stainless steel belongs to the iron alloys classification, while 6101B aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is AISI 301LN stainless steel and the bottom bar is 6101B aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 68 |
| Elongation at Break, % | 23 to 51 | |
| 9.1 to 13 |
| Fatigue Strength, MPa | 270 to 520 | |
| 62 to 70 |
| Poisson's Ratio | 0.28 | |
| 0.33 |
| Shear Modulus, GPa | 77 | |
| 26 |
| Shear Strength, MPa | 450 to 670 | |
| 120 to 150 |
| Tensile Strength: Ultimate (UTS), MPa | 630 to 1060 | |
| 190 to 250 |
| Tensile Strength: Yield (Proof), MPa | 270 to 770 | |
| 140 to 180 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 890 | |
| 160 |
| Melting Completion (Liquidus), °C | 1430 | |
| 640 |
| Melting Onset (Solidus), °C | 1380 | |
| 630 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 900 |
| Thermal Conductivity, W/m-K | 15 | |
| 210 |
| Thermal Expansion, µm/m-K | 16 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 57 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 190 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 13 | |
| 9.5 |
| Density, g/cm3 | 7.8 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 8.3 |
| Embodied Energy, MJ/kg | 39 | |
| 150 |
| Embodied Water, L/kg | 130 | |
| 1190 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 220 to 290 | |
| 20 to 23 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 to 1520 | |
| 140 to 240 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 50 |
| Strength to Weight: Axial, points | 22 to 38 | |
| 20 to 25 |
| Strength to Weight: Bending, points | 21 to 30 | |
| 27 to 32 |
| Thermal Diffusivity, mm2/s | 4.0 | |
| 87 |
| Thermal Shock Resistance, points | 14 to 24 | |
| 8.5 to 11 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 98.2 to 99.3 |
| Carbon (C), % | 0 to 0.030 | |
| 0 |
| Chromium (Cr), % | 16 to 18 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.050 |
| Iron (Fe), % | 70.7 to 77.9 | |
| 0.1 to 0.3 |
| Magnesium (Mg), % | 0 | |
| 0.35 to 0.6 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 to 0.050 |
| Nickel (Ni), % | 6.0 to 8.0 | |
| 0 |
| Nitrogen (N), % | 0.070 to 0.2 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0.3 to 0.6 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.1 |
| Residuals, % | 0 | |
| 0 to 0.1 |