AISI 301LN Stainless Steel vs. AISI 316Ti Stainless Steel
Both AISI 301LN stainless steel and AISI 316Ti stainless steel are iron alloys. They have a moderately high 92% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is AISI 301LN stainless steel and the bottom bar is AISI 316Ti stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 210 to 320 | |
| 190 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Elongation at Break, % | 23 to 51 | |
| 41 |
| Fatigue Strength, MPa | 270 to 520 | |
| 200 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 77 | |
| 82 |
| Shear Strength, MPa | 450 to 670 | |
| 400 |
| Tensile Strength: Ultimate (UTS), MPa | 630 to 1060 | |
| 580 |
| Tensile Strength: Yield (Proof), MPa | 270 to 770 | |
| 230 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 290 |
| Maximum Temperature: Corrosion, °C | 410 | |
| 470 |
| Maximum Temperature: Mechanical, °C | 890 | |
| 940 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1450 |
| Melting Onset (Solidus), °C | 1380 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 15 | |
| 15 |
| Thermal Expansion, µm/m-K | 16 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 2.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 2.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 13 | |
| 19 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 4.0 |
| Embodied Energy, MJ/kg | 39 | |
| 55 |
| Embodied Water, L/kg | 130 | |
| 150 |
Common Calculations
| PREN (Pitting Resistance) | 19 | |
| 26 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 220 to 290 | |
| 190 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 to 1520 | |
| 140 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 22 to 38 | |
| 20 |
| Strength to Weight: Bending, points | 21 to 30 | |
| 20 |
| Thermal Diffusivity, mm2/s | 4.0 | |
| 4.0 |
| Thermal Shock Resistance, points | 14 to 24 | |
| 13 |
Alloy Composition
| Carbon (C), % | 0 to 0.030 | |
| 0 to 0.080 |
| Chromium (Cr), % | 16 to 18 | |
| 16 to 18 |
| Iron (Fe), % | 70.7 to 77.9 | |
| 61.3 to 72 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0 | |
| 2.0 to 3.0 |
| Nickel (Ni), % | 6.0 to 8.0 | |
| 10 to 14 |
| Nitrogen (N), % | 0.070 to 0.2 | |
| 0 to 0.1 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.75 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0 | |
| 0 to 0.7 |