AISI 301LN Stainless Steel vs. CC496K Bronze
AISI 301LN stainless steel belongs to the iron alloys classification, while CC496K bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is AISI 301LN stainless steel and the bottom bar is CC496K bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 210 to 320 | |
| 72 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 97 |
| Elongation at Break, % | 23 to 51 | |
| 8.6 |
| Poisson's Ratio | 0.28 | |
| 0.35 |
| Shear Modulus, GPa | 77 | |
| 36 |
| Tensile Strength: Ultimate (UTS), MPa | 630 to 1060 | |
| 210 |
| Tensile Strength: Yield (Proof), MPa | 270 to 770 | |
| 99 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 890 | |
| 140 |
| Melting Completion (Liquidus), °C | 1430 | |
| 900 |
| Melting Onset (Solidus), °C | 1380 | |
| 820 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 340 |
| Thermal Conductivity, W/m-K | 15 | |
| 52 |
| Thermal Expansion, µm/m-K | 16 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 11 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 13 | |
| 31 |
| Density, g/cm3 | 7.8 | |
| 9.2 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 3.3 |
| Embodied Energy, MJ/kg | 39 | |
| 52 |
| Embodied Water, L/kg | 130 | |
| 380 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 220 to 290 | |
| 15 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 to 1520 | |
| 50 |
| Stiffness to Weight: Axial, points | 14 | |
| 5.9 |
| Stiffness to Weight: Bending, points | 25 | |
| 17 |
| Strength to Weight: Axial, points | 22 to 38 | |
| 6.5 |
| Strength to Weight: Bending, points | 21 to 30 | |
| 8.6 |
| Thermal Diffusivity, mm2/s | 4.0 | |
| 17 |
| Thermal Shock Resistance, points | 14 to 24 | |
| 8.1 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.010 |
| Antimony (Sb), % | 0 | |
| 0 to 0.5 |
| Carbon (C), % | 0 to 0.030 | |
| 0 |
| Chromium (Cr), % | 16 to 18 | |
| 0 |
| Copper (Cu), % | 0 | |
| 72 to 79.5 |
| Iron (Fe), % | 70.7 to 77.9 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 | |
| 13 to 17 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 to 0.2 |
| Nickel (Ni), % | 6.0 to 8.0 | |
| 0.5 to 2.0 |
| Nitrogen (N), % | 0.070 to 0.2 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.1 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.010 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.1 |
| Tin (Sn), % | 0 | |
| 6.0 to 8.0 |
| Zinc (Zn), % | 0 | |
| 0 to 2.0 |