AISI 301LN Stainless Steel vs. ZA-8
AISI 301LN stainless steel belongs to the iron alloys classification, while ZA-8 belongs to the zinc alloys. There are 31 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is AISI 301LN stainless steel and the bottom bar is ZA-8.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 210 to 320 | |
| 87 to 100 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 85 to 86 |
| Elongation at Break, % | 23 to 51 | |
| 1.3 to 8.0 |
| Fatigue Strength, MPa | 270 to 520 | |
| 51 to 100 |
| Poisson's Ratio | 0.28 | |
| 0.26 |
| Shear Modulus, GPa | 77 | |
| 34 |
| Shear Strength, MPa | 450 to 670 | |
| 240 to 280 |
| Tensile Strength: Ultimate (UTS), MPa | 630 to 1060 | |
| 210 to 370 |
| Tensile Strength: Yield (Proof), MPa | 270 to 770 | |
| 210 to 290 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 110 |
| Maximum Temperature: Mechanical, °C | 890 | |
| 100 |
| Melting Completion (Liquidus), °C | 1430 | |
| 400 |
| Melting Onset (Solidus), °C | 1380 | |
| 380 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 440 |
| Thermal Conductivity, W/m-K | 15 | |
| 120 |
| Thermal Expansion, µm/m-K | 16 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 28 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 40 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 13 | |
| 11 |
| Density, g/cm3 | 7.8 | |
| 6.3 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 3.3 |
| Embodied Energy, MJ/kg | 39 | |
| 62 |
| Embodied Water, L/kg | 130 | |
| 420 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 220 to 290 | |
| 2.8 to 28 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 to 1520 | |
| 260 to 490 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 22 to 38 | |
| 9.3 to 17 |
| Strength to Weight: Bending, points | 21 to 30 | |
| 12 to 18 |
| Thermal Diffusivity, mm2/s | 4.0 | |
| 42 |
| Thermal Shock Resistance, points | 14 to 24 | |
| 7.6 to 13 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 8.0 to 8.8 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0060 |
| Carbon (C), % | 0 to 0.030 | |
| 0 |
| Chromium (Cr), % | 16 to 18 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0.8 to 1.3 |
| Iron (Fe), % | 70.7 to 77.9 | |
| 0 to 0.075 |
| Lead (Pb), % | 0 | |
| 0 to 0.0060 |
| Magnesium (Mg), % | 0 | |
| 0.015 to 0.030 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 |
| Nickel (Ni), % | 6.0 to 8.0 | |
| 0 to 0.020 |
| Nitrogen (N), % | 0.070 to 0.2 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.045 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.0030 |
| Zinc (Zn), % | 0 | |
| 89.7 to 91.2 |