AISI 302 Stainless Steel vs. Type 4 Niobium
AISI 302 stainless steel belongs to the iron alloys classification, while Type 4 niobium belongs to the otherwise unclassified metals. There are 21 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is AISI 302 stainless steel and the bottom bar is Type 4 niobium.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 170 to 440 | |
| 120 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 110 |
| Elongation at Break, % | 4.5 to 46 | |
| 23 |
| Poisson's Ratio | 0.28 | |
| 0.4 |
| Shear Modulus, GPa | 77 | |
| 38 |
| Tensile Strength: Ultimate (UTS), MPa | 580 to 1430 | |
| 220 |
| Tensile Strength: Yield (Proof), MPa | 230 to 1100 | |
| 140 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 310 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 270 |
| Thermal Conductivity, W/m-K | 16 | |
| 42 |
| Thermal Expansion, µm/m-K | 17 | |
| 7.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 8.6 |
| Embodied Water, L/kg | 140 | |
| 160 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 59 to 260 | |
| 44 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 to 3070 | |
| 93 |
| Stiffness to Weight: Axial, points | 14 | |
| 6.8 |
| Stiffness to Weight: Bending, points | 25 | |
| 18 |
| Strength to Weight: Axial, points | 21 to 51 | |
| 7.2 |
| Strength to Weight: Bending, points | 20 to 36 | |
| 9.5 |
| Thermal Diffusivity, mm2/s | 4.4 | |
| 18 |
| Thermal Shock Resistance, points | 12 to 31 | |
| 21 |
Alloy Composition
| Carbon (C), % | 0 to 0.15 | |
| 0 to 0.010 |
| Chromium (Cr), % | 17 to 19 | |
| 0 |
| Hafnium (Hf), % | 0 | |
| 0 to 0.020 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0015 |
| Iron (Fe), % | 67.9 to 75 | |
| 0 to 0.010 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.050 |
| Nickel (Ni), % | 8.0 to 10 | |
| 0 to 0.0050 |
| Niobium (Nb), % | 0 | |
| 98.1 to 99.2 |
| Nitrogen (N), % | 0 to 0.1 | |
| 0 to 0.010 |
| Oxygen (O), % | 0 | |
| 0 to 0.025 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 |
| Silicon (Si), % | 0 to 0.75 | |
| 0 to 0.0050 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tantalum (Ta), % | 0 | |
| 0 to 0.5 |
| Titanium (Ti), % | 0 | |
| 0 to 0.020 |
| Tungsten (W), % | 0 | |
| 0 to 0.050 |
| Zirconium (Zr), % | 0 | |
| 0.8 to 1.2 |