AISI 302 Stainless Steel vs. C10700 Copper

AISI 302 stainless steel belongs to the iron alloys classification, while C10700 copper belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AISI 302 stainless steel and the bottom bar is C10700 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
120
Elongation at Break, % 4.5 to 46
2.2 to 50
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 77
43
Shear Strength, MPa 400 to 830
160 to 240
Tensile Strength: Ultimate (UTS), MPa 580 to 1430
230 to 410
Tensile Strength: Yield (Proof), MPa 230 to 1100
77 to 410

Thermal Properties

Latent Heat of Fusion, J/g 280
210
Maximum Temperature: Mechanical, °C 710
200
Melting Completion (Liquidus), °C 1420
1080
Melting Onset (Solidus), °C 1400
1080
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 16
390
Thermal Expansion, µm/m-K 17
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
100
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
100

Otherwise Unclassified Properties

Base Metal Price, % relative 15
35
Density, g/cm3 7.8
9.0
Embodied Carbon, kg CO2/kg material 3.0
2.7
Embodied Energy, MJ/kg 42
42
Embodied Water, L/kg 140
390

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 59 to 260
7.9 to 91
Resilience: Unit (Modulus of Resilience), kJ/m3 140 to 3070
25 to 710
Stiffness to Weight: Axial, points 14
7.2
Stiffness to Weight: Bending, points 25
18
Strength to Weight: Axial, points 21 to 51
7.2 to 13
Strength to Weight: Bending, points 20 to 36
9.4 to 14
Thermal Diffusivity, mm2/s 4.4
110
Thermal Shock Resistance, points 12 to 31
8.2 to 15

Alloy Composition

Carbon (C), % 0 to 0.15
0
Chromium (Cr), % 17 to 19
0
Copper (Cu), % 0
99.83 to 99.915
Iron (Fe), % 67.9 to 75
0
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 8.0 to 10
0
Nitrogen (N), % 0 to 0.1
0
Oxygen (O), % 0
0 to 0.0010
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 0.75
0
Silver (Ag), % 0
0.085 to 0.12
Sulfur (S), % 0 to 0.030
0
Residuals, % 0
0 to 0.050