AISI 302 Stainless Steel vs. C33500 Brass
AISI 302 stainless steel belongs to the iron alloys classification, while C33500 brass belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is AISI 302 stainless steel and the bottom bar is C33500 brass.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 200 | |
100 |
Elongation at Break, % | 4.5 to 46 | |
3.0 to 28 |
Poisson's Ratio | 0.28 | |
0.31 |
Shear Modulus, GPa | 77 | |
40 |
Shear Strength, MPa | 400 to 830 | |
220 to 360 |
Tensile Strength: Ultimate (UTS), MPa | 580 to 1430 | |
340 to 650 |
Tensile Strength: Yield (Proof), MPa | 230 to 1100 | |
120 to 420 |
Thermal Properties
Latent Heat of Fusion, J/g | 280 | |
170 |
Maximum Temperature: Mechanical, °C | 710 | |
120 |
Melting Completion (Liquidus), °C | 1420 | |
930 |
Melting Onset (Solidus), °C | 1400 | |
900 |
Specific Heat Capacity, J/kg-K | 480 | |
390 |
Thermal Conductivity, W/m-K | 16 | |
120 |
Thermal Expansion, µm/m-K | 17 | |
20 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
26 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 2.8 | |
29 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 15 | |
24 |
Density, g/cm3 | 7.8 | |
8.1 |
Embodied Carbon, kg CO2/kg material | 3.0 | |
2.7 |
Embodied Energy, MJ/kg | 42 | |
45 |
Embodied Water, L/kg | 140 | |
320 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 59 to 260 | |
8.0 to 160 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 to 3070 | |
69 to 860 |
Stiffness to Weight: Axial, points | 14 | |
7.2 |
Stiffness to Weight: Bending, points | 25 | |
19 |
Strength to Weight: Axial, points | 21 to 51 | |
12 to 22 |
Strength to Weight: Bending, points | 20 to 36 | |
13 to 21 |
Thermal Diffusivity, mm2/s | 4.4 | |
37 |
Thermal Shock Resistance, points | 12 to 31 | |
11 to 22 |
Alloy Composition
Carbon (C), % | 0 to 0.15 | |
0 |
Chromium (Cr), % | 17 to 19 | |
0 |
Copper (Cu), % | 0 | |
62 to 65 |
Iron (Fe), % | 67.9 to 75 | |
0 to 0.1 |
Lead (Pb), % | 0 | |
0.25 to 0.7 |
Manganese (Mn), % | 0 to 2.0 | |
0 |
Nickel (Ni), % | 8.0 to 10 | |
0 |
Nitrogen (N), % | 0 to 0.1 | |
0 |
Phosphorus (P), % | 0 to 0.045 | |
0 |
Silicon (Si), % | 0 to 0.75 | |
0 |
Sulfur (S), % | 0 to 0.030 | |
0 |
Zinc (Zn), % | 0 | |
33.8 to 37.8 |
Residuals, % | 0 | |
0 to 0.4 |