AISI 303 Stainless Steel vs. EN 1.4005 Stainless Steel
Both AISI 303 stainless steel and EN 1.4005 stainless steel are iron alloys. They have 86% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is AISI 303 stainless steel and the bottom bar is EN 1.4005 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 40 to 51 | |
| 13 to 21 |
| Fatigue Strength, MPa | 230 to 360 | |
| 240 to 290 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 77 | |
| 76 |
| Shear Strength, MPa | 430 to 470 | |
| 390 to 450 |
| Tensile Strength: Ultimate (UTS), MPa | 600 to 690 | |
| 630 to 750 |
| Tensile Strength: Yield (Proof), MPa | 230 to 420 | |
| 370 to 500 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 270 |
| Maximum Temperature: Corrosion, °C | 410 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 930 | |
| 760 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1440 |
| Melting Onset (Solidus), °C | 1400 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Conductivity, W/m-K | 16 | |
| 30 |
| Thermal Expansion, µm/m-K | 17 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 2.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.8 | |
| 3.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 15 | |
| 7.0 |
| Density, g/cm3 | 7.8 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 2.0 |
| Embodied Energy, MJ/kg | 42 | |
| 28 |
| Embodied Water, L/kg | 140 | |
| 100 |
Common Calculations
| PREN (Pitting Resistance) | 18 | |
| 14 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 240 | |
| 90 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 to 440 | |
| 350 to 650 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 21 to 25 | |
| 23 to 27 |
| Strength to Weight: Bending, points | 20 to 22 | |
| 21 to 24 |
| Thermal Diffusivity, mm2/s | 4.4 | |
| 8.1 |
| Thermal Shock Resistance, points | 13 to 15 | |
| 23 to 27 |
Alloy Composition
| Carbon (C), % | 0 to 0.15 | |
| 0.060 to 0.15 |
| Chromium (Cr), % | 17 to 19 | |
| 12 to 14 |
| Iron (Fe), % | 67.3 to 74.9 | |
| 82.4 to 87.8 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.6 |
| Nickel (Ni), % | 8.0 to 10 | |
| 0 |
| Phosphorus (P), % | 0 to 0.2 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0.15 to 0.35 | |
| 0.15 to 0.35 |