AISI 303 Stainless Steel vs. C71520 Copper-nickel
AISI 303 stainless steel belongs to the iron alloys classification, while C71520 copper-nickel belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is AISI 303 stainless steel and the bottom bar is C71520 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 140 |
| Elongation at Break, % | 40 to 51 | |
| 10 to 45 |
| Poisson's Ratio | 0.28 | |
| 0.33 |
| Shear Modulus, GPa | 77 | |
| 51 |
| Shear Strength, MPa | 430 to 470 | |
| 250 to 340 |
| Tensile Strength: Ultimate (UTS), MPa | 600 to 690 | |
| 370 to 570 |
| Tensile Strength: Yield (Proof), MPa | 230 to 420 | |
| 140 to 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 230 |
| Maximum Temperature: Mechanical, °C | 930 | |
| 260 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1170 |
| Melting Onset (Solidus), °C | 1400 | |
| 1120 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 400 |
| Thermal Conductivity, W/m-K | 16 | |
| 32 |
| Thermal Expansion, µm/m-K | 17 | |
| 15 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 5.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.8 | |
| 5.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 15 | |
| 40 |
| Density, g/cm3 | 7.8 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 5.0 |
| Embodied Energy, MJ/kg | 42 | |
| 73 |
| Embodied Water, L/kg | 140 | |
| 280 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 240 | |
| 54 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 to 440 | |
| 67 to 680 |
| Stiffness to Weight: Axial, points | 14 | |
| 8.6 |
| Stiffness to Weight: Bending, points | 25 | |
| 19 |
| Strength to Weight: Axial, points | 21 to 25 | |
| 12 to 18 |
| Strength to Weight: Bending, points | 20 to 22 | |
| 13 to 17 |
| Thermal Diffusivity, mm2/s | 4.4 | |
| 8.9 |
| Thermal Shock Resistance, points | 13 to 15 | |
| 12 to 19 |
Alloy Composition
| Carbon (C), % | 0 to 0.15 | |
| 0 to 0.050 |
| Chromium (Cr), % | 17 to 19 | |
| 0 |
| Copper (Cu), % | 0 | |
| 65 to 71.6 |
| Iron (Fe), % | 67.3 to 74.9 | |
| 0.4 to 1.0 |
| Lead (Pb), % | 0 | |
| 0 to 0.020 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 8.0 to 10 | |
| 28 to 33 |
| Phosphorus (P), % | 0 to 0.2 | |
| 0 to 0.2 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0.15 to 0.35 | |
| 0 to 0.020 |
| Zinc (Zn), % | 0 | |
| 0 to 0.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |