AISI 303Se Stainless Steel vs. EN 1.4162 Stainless Steel

Both AISI 303Se stainless steel and EN 1.4162 stainless steel are iron alloys. They have a moderately high 91% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AISI 303Se stainless steel and the bottom bar is EN 1.4162 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
250
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 45
32
Fatigue Strength, MPa 210
410
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
78
Shear Strength, MPa 410
520
Tensile Strength: Ultimate (UTS), MPa 590
780
Tensile Strength: Yield (Proof), MPa 230
520

Thermal Properties

Latent Heat of Fusion, J/g 290
290
Maximum Temperature: Corrosion, °C 410
430
Maximum Temperature: Mechanical, °C 930
1000
Melting Completion (Liquidus), °C 1420
1420
Melting Onset (Solidus), °C 1380
1370
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 16
15
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 16
12
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 3.0
2.6
Embodied Energy, MJ/kg 42
38
Embodied Water, L/kg 140
150

Common Calculations

PREN (Pitting Resistance) 18
27
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
220
Resilience: Unit (Modulus of Resilience), kJ/m3 130
690
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
28
Strength to Weight: Bending, points 20
25
Thermal Diffusivity, mm2/s 4.3
4.0
Thermal Shock Resistance, points 13
21

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.040
Chromium (Cr), % 17 to 19
21 to 22
Copper (Cu), % 0
0.1 to 0.8
Iron (Fe), % 67.2 to 74.9
67.2 to 73.3
Manganese (Mn), % 0 to 2.0
4.0 to 6.0
Molybdenum (Mo), % 0
0.1 to 0.8
Nickel (Ni), % 8.0 to 10
1.4 to 1.9
Nitrogen (N), % 0
0.2 to 0.25
Phosphorus (P), % 0 to 0.2
0 to 0.040
Selenium (Se), % 0.15 to 0.35
0
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.060
0 to 0.015