AISI 303Se Stainless Steel vs. EN 1.4520 Stainless Steel

Both AISI 303Se stainless steel and EN 1.4520 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 89% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is AISI 303Se stainless steel and the bottom bar is EN 1.4520 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
180
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 45
26
Fatigue Strength, MPa 210
160
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Shear Strength, MPa 410
310
Tensile Strength: Ultimate (UTS), MPa 590
480
Tensile Strength: Yield (Proof), MPa 230
220

Thermal Properties

Latent Heat of Fusion, J/g 290
280
Maximum Temperature: Corrosion, °C 410
500
Maximum Temperature: Mechanical, °C 930
870
Melting Completion (Liquidus), °C 1420
1440
Melting Onset (Solidus), °C 1380
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 16
20
Thermal Expansion, µm/m-K 16
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 16
8.5
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 3.0
2.2
Embodied Energy, MJ/kg 42
32
Embodied Water, L/kg 140
120

Common Calculations

PREN (Pitting Resistance) 18
17
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
100
Resilience: Unit (Modulus of Resilience), kJ/m3 130
120
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
17
Strength to Weight: Bending, points 20
18
Thermal Diffusivity, mm2/s 4.3
5.4
Thermal Shock Resistance, points 13
17

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.025
Chromium (Cr), % 17 to 19
16 to 18
Iron (Fe), % 67.2 to 74.9
80.1 to 83.9
Manganese (Mn), % 0 to 2.0
0 to 0.5
Nickel (Ni), % 8.0 to 10
0
Nitrogen (N), % 0
0 to 0.015
Phosphorus (P), % 0 to 0.2
0 to 0.040
Selenium (Se), % 0.15 to 0.35
0
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.060
0 to 0.015
Titanium (Ti), % 0
0.15 to 0.8