AISI 303Se Stainless Steel vs. C62300 Bronze

AISI 303Se stainless steel belongs to the iron alloys classification, while C62300 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AISI 303Se stainless steel and the bottom bar is C62300 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 45
18 to 32
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 77
43
Shear Strength, MPa 410
360 to 390
Tensile Strength: Ultimate (UTS), MPa 590
570 to 630
Tensile Strength: Yield (Proof), MPa 230
230 to 310

Thermal Properties

Latent Heat of Fusion, J/g 290
230
Maximum Temperature: Mechanical, °C 930
220
Melting Completion (Liquidus), °C 1420
1050
Melting Onset (Solidus), °C 1380
1040
Specific Heat Capacity, J/kg-K 480
440
Thermal Conductivity, W/m-K 16
54
Thermal Expansion, µm/m-K 16
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
12
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
13

Otherwise Unclassified Properties

Base Metal Price, % relative 16
28
Density, g/cm3 7.8
8.3
Embodied Carbon, kg CO2/kg material 3.0
3.1
Embodied Energy, MJ/kg 42
52
Embodied Water, L/kg 140
390

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
95 to 150
Resilience: Unit (Modulus of Resilience), kJ/m3 130
240 to 430
Stiffness to Weight: Axial, points 14
7.6
Stiffness to Weight: Bending, points 25
19
Strength to Weight: Axial, points 21
19 to 21
Strength to Weight: Bending, points 20
18 to 20
Thermal Diffusivity, mm2/s 4.3
15
Thermal Shock Resistance, points 13
20 to 22

Alloy Composition

Aluminum (Al), % 0
8.5 to 10
Carbon (C), % 0 to 0.15
0
Chromium (Cr), % 17 to 19
0
Copper (Cu), % 0
83.2 to 89.5
Iron (Fe), % 67.2 to 74.9
2.0 to 4.0
Manganese (Mn), % 0 to 2.0
0 to 0.5
Nickel (Ni), % 8.0 to 10
0 to 1.0
Phosphorus (P), % 0 to 0.2
0
Selenium (Se), % 0.15 to 0.35
0
Silicon (Si), % 0 to 1.0
0 to 0.25
Sulfur (S), % 0 to 0.060
0
Tin (Sn), % 0
0 to 0.6
Residuals, % 0
0 to 0.5