AISI 304LN Stainless Steel vs. C90200 Bronze

AISI 304LN stainless steel belongs to the iron alloys classification, while C90200 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AISI 304LN stainless steel and the bottom bar is C90200 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190 to 350
70
Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 7.8 to 46
30
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 77
41
Tensile Strength: Ultimate (UTS), MPa 580 to 1160
260
Tensile Strength: Yield (Proof), MPa 230 to 870
110

Thermal Properties

Latent Heat of Fusion, J/g 290
200
Maximum Temperature: Mechanical, °C 960
180
Melting Completion (Liquidus), °C 1420
1050
Melting Onset (Solidus), °C 1380
880
Specific Heat Capacity, J/kg-K 480
370
Thermal Conductivity, W/m-K 15
62
Thermal Expansion, µm/m-K 16
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
13
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
13

Otherwise Unclassified Properties

Base Metal Price, % relative 16
34
Density, g/cm3 7.8
8.8
Embodied Carbon, kg CO2/kg material 3.1
3.3
Embodied Energy, MJ/kg 44
53
Embodied Water, L/kg 150
370

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 83 to 270
63
Resilience: Unit (Modulus of Resilience), kJ/m3 140 to 1900
55
Stiffness to Weight: Axial, points 14
7.0
Stiffness to Weight: Bending, points 25
18
Strength to Weight: Axial, points 21 to 41
8.3
Strength to Weight: Bending, points 20 to 31
10
Thermal Diffusivity, mm2/s 4.0
19
Thermal Shock Resistance, points 13 to 26
9.5

Alloy Composition

Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
0 to 0.2
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 18 to 20
0
Copper (Cu), % 0
91 to 94
Iron (Fe), % 65 to 73.9
0 to 0.2
Lead (Pb), % 0
0 to 0.3
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 8.0 to 12
0 to 0.5
Nitrogen (N), % 0.1 to 0.16
0
Phosphorus (P), % 0 to 0.045
0 to 0.050
Silicon (Si), % 0 to 0.75
0 to 0.0050
Sulfur (S), % 0 to 0.030
0 to 0.050
Tin (Sn), % 0
6.0 to 8.0
Zinc (Zn), % 0
0 to 0.5
Residuals, % 0
0 to 0.6