Both AISI 304N stainless steel and ASTM A369 grade FP91 are iron alloys. They have 80% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is AISI 304N stainless steel and the bottom bar is ASTM A369 grade FP91.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190 to 360
200
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 9.1 to 45
19
Fatigue Strength, MPa 220 to 440
320
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
75
Shear Strength, MPa 420 to 700
410
Tensile Strength: Ultimate (UTS), MPa 620 to 1180
670
Tensile Strength: Yield (Proof), MPa 270 to 850
460

Thermal Properties

Latent Heat of Fusion, J/g 290
270
Maximum Temperature: Mechanical, °C 960
600
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
26
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
8.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
10

Otherwise Unclassified Properties

Base Metal Price, % relative 15
7.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.0
2.6
Embodied Energy, MJ/kg 43
37
Embodied Water, L/kg 150
88

Common Calculations

PREN (Pitting Resistance) 21
13
Resilience: Ultimate (Unit Rupture Work), MJ/m3 98 to 280
110
Resilience: Unit (Modulus of Resilience), kJ/m3 180 to 1830
560
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22 to 42
24
Strength to Weight: Bending, points 21 to 32
22
Thermal Diffusivity, mm2/s 4.2
6.9
Thermal Shock Resistance, points 14 to 26
18

Alloy Composition

Aluminum (Al), % 0
0 to 0.020
Carbon (C), % 0 to 0.080
0.080 to 0.12
Chromium (Cr), % 18 to 20
8.0 to 9.5
Iron (Fe), % 66.4 to 73.9
87.3 to 90.3
Manganese (Mn), % 0 to 2.0
0.3 to 0.6
Molybdenum (Mo), % 0
0.85 to 1.1
Nickel (Ni), % 8.0 to 10.5
0 to 0.4
Niobium (Nb), % 0
0.060 to 0.1
Nitrogen (N), % 0.1 to 0.16
0.030 to 0.070
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 0.75
0.2 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.025
Titanium (Ti), % 0
0 to 0.010
Vanadium (V), % 0
0.18 to 0.25
Zirconium (Zr), % 0
0 to 0.010