AISI 305 Stainless Steel vs. 88-silver 12-tin-oxide
AISI 305 stainless steel belongs to the iron alloys classification, while 88-silver 12-tin-oxide belongs to the otherwise unclassified metals. There are 6 material properties with values for both materials. Properties with values for just one material (28, in this case) are not shown.
For each property being compared, the top bar is AISI 305 stainless steel and the bottom bar is 88-silver 12-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 84 to 86 |
| Elongation at Break, % | 34 to 45 | |
| 9.0 to 37 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 200 to 210 | |
| 24 to 70 |
| Shear Strength, MPa | 400 to 470 | |
| 150 to 160 |
| Tensile Strength: Ultimate (UTS), MPa | 580 to 710 | |
| 230 to 280 |
| Tensile Strength: Yield (Proof), MPa | 230 to 350 | |
| 110 to 260 |