AISI 305 Stainless Steel vs. 92-silver 8-tin-oxide
AISI 305 stainless steel belongs to the iron alloys classification, while 92-silver 8-tin-oxide belongs to the otherwise unclassified metals. There are 6 material properties with values for both materials. Properties with values for just one material (28, in this case) are not shown.
For each property being compared, the top bar is AISI 305 stainless steel and the bottom bar is 92-silver 8-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 76 to 80 |
| Elongation at Break, % | 34 to 45 | |
| 32 to 34 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 200 to 210 | |
| 62 to 110 |
| Shear Strength, MPa | 400 to 470 | |
| 150 to 210 |
| Tensile Strength: Ultimate (UTS), MPa | 580 to 710 | |
| 230 to 320 |
| Tensile Strength: Yield (Proof), MPa | 230 to 350 | |
| 120 to 300 |