AISI 305 Stainless Steel vs. EN 1.4606 Stainless Steel
Both AISI 305 stainless steel and EN 1.4606 stainless steel are iron alloys. They have 82% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is AISI 305 stainless steel and the bottom bar is EN 1.4606 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 34 to 45 | |
| 23 to 39 |
| Fatigue Strength, MPa | 210 to 280 | |
| 240 to 420 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 75 |
| Shear Strength, MPa | 400 to 470 | |
| 410 to 640 |
| Tensile Strength: Ultimate (UTS), MPa | 580 to 710 | |
| 600 to 1020 |
| Tensile Strength: Yield (Proof), MPa | 230 to 350 | |
| 280 to 630 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 300 |
| Maximum Temperature: Corrosion, °C | 410 | |
| 770 |
| Maximum Temperature: Mechanical, °C | 540 | |
| 910 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1430 |
| Melting Onset (Solidus), °C | 1400 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 16 | |
| 14 |
| Thermal Expansion, µm/m-K | 17 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 1.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 2.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 16 | |
| 26 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 3.2 | |
| 6.0 |
| Embodied Energy, MJ/kg | 45 | |
| 87 |
| Embodied Water, L/kg | 150 | |
| 170 |
Common Calculations
| PREN (Pitting Resistance) | 18 | |
| 19 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 200 to 210 | |
| 190 to 200 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 to 320 | |
| 200 to 1010 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 20 to 25 | |
| 21 to 36 |
| Strength to Weight: Bending, points | 20 to 23 | |
| 20 to 28 |
| Thermal Diffusivity, mm2/s | 4.2 | |
| 3.7 |
| Thermal Shock Resistance, points | 13 to 15 | |
| 21 to 35 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.35 |
| Boron (B), % | 0 | |
| 0.0010 to 0.010 |
| Carbon (C), % | 0 to 0.12 | |
| 0 to 0.080 |
| Chromium (Cr), % | 17 to 19 | |
| 13 to 16 |
| Iron (Fe), % | 65.1 to 72.5 | |
| 49.2 to 59 |
| Manganese (Mn), % | 0 to 2.0 | |
| 1.0 to 2.0 |
| Molybdenum (Mo), % | 0 | |
| 1.0 to 1.5 |
| Nickel (Ni), % | 10.5 to 13 | |
| 24 to 27 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.75 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 | |
| 1.9 to 2.3 |
| Vanadium (V), % | 0 | |
| 0.1 to 0.5 |