AISI 305 Stainless Steel vs. C26000 Brass
AISI 305 stainless steel belongs to the iron alloys classification, while C26000 brass belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is AISI 305 stainless steel and the bottom bar is C26000 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 110 |
| Elongation at Break, % | 34 to 45 | |
| 2.5 to 66 |
| Poisson's Ratio | 0.28 | |
| 0.31 |
| Shear Modulus, GPa | 77 | |
| 41 |
| Shear Strength, MPa | 400 to 470 | |
| 230 to 390 |
| Tensile Strength: Ultimate (UTS), MPa | 580 to 710 | |
| 320 to 680 |
| Tensile Strength: Yield (Proof), MPa | 230 to 350 | |
| 110 to 570 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 180 |
| Maximum Temperature: Mechanical, °C | 540 | |
| 140 |
| Melting Completion (Liquidus), °C | 1450 | |
| 950 |
| Melting Onset (Solidus), °C | 1400 | |
| 920 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 390 |
| Thermal Conductivity, W/m-K | 16 | |
| 120 |
| Thermal Expansion, µm/m-K | 17 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 28 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 31 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 16 | |
| 25 |
| Density, g/cm3 | 7.8 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 3.2 | |
| 2.7 |
| Embodied Energy, MJ/kg | 45 | |
| 45 |
| Embodied Water, L/kg | 150 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 200 to 210 | |
| 6.1 to 420 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 to 320 | |
| 51 to 1490 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 25 | |
| 19 |
| Strength to Weight: Axial, points | 20 to 25 | |
| 11 to 23 |
| Strength to Weight: Bending, points | 20 to 23 | |
| 13 to 21 |
| Thermal Diffusivity, mm2/s | 4.2 | |
| 38 |
| Thermal Shock Resistance, points | 13 to 15 | |
| 11 to 23 |
Alloy Composition
| Bismuth (Bi), % | 0 | |
| 0 to 0.0059 |
| Carbon (C), % | 0 to 0.12 | |
| 0 |
| Chromium (Cr), % | 17 to 19 | |
| 0 |
| Copper (Cu), % | 0 | |
| 68.5 to 71.5 |
| Iron (Fe), % | 65.1 to 72.5 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 | |
| 0 to 0.070 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 |
| Nickel (Ni), % | 10.5 to 13 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 |
| Silicon (Si), % | 0 to 0.75 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 28.1 to 31.5 |
| Residuals, % | 0 | |
| 0 to 0.3 |