AISI 308L Stainless Steel vs. EN 1.4876 Stainless Steel

Both AISI 308L stainless steel and EN 1.4876 stainless steel are iron alloys. They have 77% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is AISI 308L stainless steel and the bottom bar is EN 1.4876 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
170
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
33
Fatigue Strength, MPa 180
150
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
77
Shear Strength, MPa 380
370
Tensile Strength: Ultimate (UTS), MPa 580
570
Tensile Strength: Yield (Proof), MPa 230
190

Thermal Properties

Latent Heat of Fusion, J/g 290
300
Maximum Temperature: Corrosion, °C 430
490
Maximum Temperature: Mechanical, °C 1010
1100
Melting Completion (Liquidus), °C 1420
1400
Melting Onset (Solidus), °C 1380
1350
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
12
Thermal Expansion, µm/m-K 16
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 16
30
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 3.2
5.3
Embodied Energy, MJ/kg 45
76
Embodied Water, L/kg 160
200

Common Calculations

PREN (Pitting Resistance) 21
21
Resilience: Ultimate (Unit Rupture Work), MJ/m3 160
140
Resilience: Unit (Modulus of Resilience), kJ/m3 140
94
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
20
Strength to Weight: Bending, points 20
19
Thermal Diffusivity, mm2/s 4.1
3.2
Thermal Shock Resistance, points 13
14

Alloy Composition

Aluminum (Al), % 0
0.15 to 0.6
Carbon (C), % 0 to 0.080
0 to 0.12
Chromium (Cr), % 19.5 to 22
19 to 23
Iron (Fe), % 63.8 to 70.5
38.6 to 50.7
Manganese (Mn), % 1.0 to 2.5
0 to 2.0
Nickel (Ni), % 9.0 to 11
30 to 34
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0.25 to 0.6
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0
0.15 to 0.6