AISI 309 Stainless Steel vs. EN 1.4412 Stainless Steel

Both AISI 309 stainless steel and EN 1.4412 stainless steel are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AISI 309 stainless steel and the bottom bar is EN 1.4412 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180 to 210
140
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34 to 47
34
Fatigue Strength, MPa 250 to 280
190
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 78
79
Tensile Strength: Ultimate (UTS), MPa 600 to 710
490
Tensile Strength: Yield (Proof), MPa 260 to 350
230

Thermal Properties

Latent Heat of Fusion, J/g 290
300
Maximum Temperature: Corrosion, °C 440
420
Maximum Temperature: Mechanical, °C 980
1000
Melting Completion (Liquidus), °C 1450
1450
Melting Onset (Solidus), °C 1400
1400
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
15
Thermal Expansion, µm/m-K 15
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 19
20
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.6
4.1
Embodied Energy, MJ/kg 51
56
Embodied Water, L/kg 170
160

Common Calculations

PREN (Pitting Resistance) 23
30
Resilience: Ultimate (Unit Rupture Work), MJ/m3 200 to 230
140
Resilience: Unit (Modulus of Resilience), kJ/m3 170 to 310
140
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21 to 25
17
Strength to Weight: Bending, points 20 to 23
18
Thermal Diffusivity, mm2/s 4.3
3.9
Thermal Shock Resistance, points 14 to 16
11

Alloy Composition

Carbon (C), % 0 to 0.2
0 to 0.070
Chromium (Cr), % 22 to 24
18 to 20
Iron (Fe), % 58 to 66
60.4 to 69
Manganese (Mn), % 0 to 2.0
0 to 1.5
Molybdenum (Mo), % 0
3.0 to 3.5
Nickel (Ni), % 12 to 15
10 to 13
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 0.75
0 to 1.5
Sulfur (S), % 0 to 0.030
0 to 0.030