AISI 309 Stainless Steel vs. S24000 Stainless Steel
Both AISI 309 stainless steel and S24000 stainless steel are iron alloys. They have 84% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is AISI 309 stainless steel and the bottom bar is S24000 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 180 to 210 | |
| 210 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Elongation at Break, % | 34 to 47 | |
| 39 |
| Fatigue Strength, MPa | 250 to 280 | |
| 370 |
| Poisson's Ratio | 0.27 | |
| 0.28 |
| Rockwell B Hardness | 84 | |
| 88 |
| Shear Modulus, GPa | 78 | |
| 77 |
| Shear Strength, MPa | 420 to 470 | |
| 530 |
| Tensile Strength: Ultimate (UTS), MPa | 600 to 710 | |
| 770 |
| Tensile Strength: Yield (Proof), MPa | 260 to 350 | |
| 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 280 |
| Maximum Temperature: Corrosion, °C | 440 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 980 | |
| 910 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1390 |
| Melting Onset (Solidus), °C | 1400 | |
| 1350 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Expansion, µm/m-K | 15 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 19 | |
| 12 |
| Density, g/cm3 | 7.8 | |
| 7.6 |
| Embodied Carbon, kg CO2/kg material | 3.6 | |
| 2.7 |
| Embodied Energy, MJ/kg | 51 | |
| 39 |
| Embodied Water, L/kg | 170 | |
| 150 |
Common Calculations
| PREN (Pitting Resistance) | 23 | |
| 23 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 200 to 230 | |
| 260 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 170 to 310 | |
| 470 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 21 to 25 | |
| 28 |
| Strength to Weight: Bending, points | 20 to 23 | |
| 24 |
| Thermal Shock Resistance, points | 14 to 16 | |
| 16 |
Alloy Composition
| Carbon (C), % | 0 to 0.2 | |
| 0 to 0.080 |
| Chromium (Cr), % | 22 to 24 | |
| 17 to 19 |
| Iron (Fe), % | 58 to 66 | |
| 61.5 to 69 |
| Manganese (Mn), % | 0 to 2.0 | |
| 11.5 to 14.5 |
| Nickel (Ni), % | 12 to 15 | |
| 2.3 to 3.7 |
| Nitrogen (N), % | 0 | |
| 0.2 to 0.4 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.060 |
| Silicon (Si), % | 0 to 0.75 | |
| 0 to 0.75 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |