AISI 309H Stainless Steel vs. ACI-ASTM CF10SMnN Steel
Both AISI 309H stainless steel and ACI-ASTM CF10SMnN steel are iron alloys. They have 89% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is AISI 309H stainless steel and the bottom bar is ACI-ASTM CF10SMnN steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 | |
| 190 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 40 | |
| 34 |
| Fatigue Strength, MPa | 200 | |
| 260 |
| Poisson's Ratio | 0.27 | |
| 0.28 |
| Shear Modulus, GPa | 78 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 580 | |
| 660 |
| Tensile Strength: Yield (Proof), MPa | 230 | |
| 330 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 340 |
| Maximum Temperature: Corrosion, °C | 440 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 1080 | |
| 900 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1360 |
| Melting Onset (Solidus), °C | 1370 | |
| 1310 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 500 |
| Thermal Expansion, µm/m-K | 16 | |
| 16 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 19 | |
| 15 |
| Density, g/cm3 | 7.8 | |
| 7.5 |
| Embodied Carbon, kg CO2/kg material | 3.6 | |
| 3.1 |
| Embodied Energy, MJ/kg | 51 | |
| 45 |
| Embodied Water, L/kg | 170 | |
| 150 |
Common Calculations
| PREN (Pitting Resistance) | 23 | |
| 19 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 190 | |
| 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 | |
| 280 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 26 |
| Strength to Weight: Axial, points | 21 | |
| 24 |
| Strength to Weight: Bending, points | 20 | |
| 22 |
| Thermal Shock Resistance, points | 13 | |
| 15 |
Alloy Composition
| Carbon (C), % | 0.040 to 0.1 | |
| 0 to 0.1 |
| Chromium (Cr), % | 22 to 24 | |
| 16 to 18 |
| Iron (Fe), % | 58.1 to 66 | |
| 59.1 to 65.4 |
| Manganese (Mn), % | 0 to 2.0 | |
| 7.0 to 9.0 |
| Nickel (Ni), % | 12 to 15 | |
| 8.0 to 9.0 |
| Nitrogen (N), % | 0 | |
| 0.080 to 0.18 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.060 |
| Silicon (Si), % | 0 to 0.75 | |
| 3.5 to 4.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |