AISI 309H Stainless Steel vs. ASTM A182 Grade FR

Both AISI 309H stainless steel and ASTM A182 grade FR are iron alloys. Both are furnished in the annealed condition. They have 65% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AISI 309H stainless steel and the bottom bar is ASTM A182 grade FR.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
170
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 40
28
Fatigue Strength, MPa 200
270
Poisson's Ratio 0.27
0.29
Reduction in Area, % 51
43
Shear Modulus, GPa 78
72
Shear Strength, MPa 400
320
Tensile Strength: Ultimate (UTS), MPa 580
490
Tensile Strength: Yield (Proof), MPa 230
360

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 1080
410
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
52
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 19
3.3
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.6
1.6
Embodied Energy, MJ/kg 51
21
Embodied Water, L/kg 170
52

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
120
Resilience: Unit (Modulus of Resilience), kJ/m3 130
340
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
17
Strength to Weight: Bending, points 20
17
Thermal Diffusivity, mm2/s 4.0
14
Thermal Shock Resistance, points 13
14

Alloy Composition

Carbon (C), % 0.040 to 0.1
0 to 0.2
Chromium (Cr), % 22 to 24
0
Copper (Cu), % 0
0.75 to 1.3
Iron (Fe), % 58.1 to 66
95.2 to 97.3
Manganese (Mn), % 0 to 2.0
0.4 to 1.1
Nickel (Ni), % 12 to 15
1.6 to 2.2
Phosphorus (P), % 0 to 0.045
0 to 0.045
Silicon (Si), % 0 to 0.75
0
Sulfur (S), % 0 to 0.030
0 to 0.050