AISI 309HCb Stainless Steel vs. 7475 Aluminum

AISI 309HCb stainless steel belongs to the iron alloys classification, while 7475 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AISI 309HCb stainless steel and the bottom bar is 7475 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
70
Elongation at Break, % 46
10 to 12
Fatigue Strength, MPa 210
190 to 210
Poisson's Ratio 0.28
0.32
Shear Modulus, GPa 78
26
Shear Strength, MPa 410
320 to 350
Tensile Strength: Ultimate (UTS), MPa 590
530 to 590
Tensile Strength: Yield (Proof), MPa 230
440 to 520

Thermal Properties

Latent Heat of Fusion, J/g 300
380
Maximum Temperature: Mechanical, °C 1090
180
Melting Completion (Liquidus), °C 1420
640
Melting Onset (Solidus), °C 1380
480
Specific Heat Capacity, J/kg-K 480
870
Thermal Conductivity, W/m-K 15
140 to 160
Thermal Expansion, µm/m-K 16
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
33 to 42
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
98 to 120

Otherwise Unclassified Properties

Base Metal Price, % relative 23
10
Density, g/cm3 7.8
3.0
Embodied Carbon, kg CO2/kg material 4.1
8.2
Embodied Energy, MJ/kg 59
150
Embodied Water, L/kg 170
1130

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
53 to 68
Resilience: Unit (Modulus of Resilience), kJ/m3 130
1390 to 1920
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
46
Strength to Weight: Axial, points 21
49 to 55
Strength to Weight: Bending, points 20
48 to 52
Thermal Diffusivity, mm2/s 4.0
53 to 63
Thermal Shock Resistance, points 13
23 to 26

Alloy Composition

Aluminum (Al), % 0
88.6 to 91.6
Carbon (C), % 0.040 to 0.1
0
Chromium (Cr), % 22 to 24
0.18 to 0.25
Copper (Cu), % 0
1.2 to 1.9
Iron (Fe), % 56 to 66
0 to 0.12
Magnesium (Mg), % 0
1.9 to 2.6
Manganese (Mn), % 0 to 2.0
0 to 0.060
Nickel (Ni), % 12 to 16
0
Niobium (Nb), % 0 to 1.1
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 0.75
0 to 0.1
Sulfur (S), % 0 to 0.030
0
Titanium (Ti), % 0
0 to 0.060
Zinc (Zn), % 0
5.1 to 6.2
Residuals, % 0
0 to 0.15