AISI 309HCb Stainless Steel vs. EN 1.4458 Stainless Steel

Both AISI 309HCb stainless steel and EN 1.4458 stainless steel are iron alloys. They have 83% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AISI 309HCb stainless steel and the bottom bar is EN 1.4458 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
150
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 46
34
Fatigue Strength, MPa 210
150
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
78
Tensile Strength: Ultimate (UTS), MPa 590
510
Tensile Strength: Yield (Proof), MPa 230
190

Thermal Properties

Latent Heat of Fusion, J/g 300
300
Maximum Temperature: Corrosion, °C 510
430
Maximum Temperature: Mechanical, °C 1090
1100
Melting Completion (Liquidus), °C 1420
1420
Melting Onset (Solidus), °C 1380
1370
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
16
Thermal Expansion, µm/m-K 16
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 23
30
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 4.1
5.4
Embodied Energy, MJ/kg 59
75
Embodied Water, L/kg 170
200

Common Calculations

PREN (Pitting Resistance) 23
30
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
140
Resilience: Unit (Modulus of Resilience), kJ/m3 130
89
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
17
Strength to Weight: Bending, points 20
18
Thermal Diffusivity, mm2/s 4.0
4.2
Thermal Shock Resistance, points 13
12

Alloy Composition

Carbon (C), % 0.040 to 0.1
0 to 0.030
Chromium (Cr), % 22 to 24
19 to 22
Copper (Cu), % 0
0 to 2.0
Iron (Fe), % 56 to 66
40.2 to 53
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0
2.0 to 2.5
Nickel (Ni), % 12 to 16
26 to 30
Niobium (Nb), % 0 to 1.1
0
Nitrogen (N), % 0
0 to 0.2
Phosphorus (P), % 0 to 0.045
0 to 0.035
Silicon (Si), % 0 to 0.75
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.025