AISI 309S Stainless Steel vs. EN 1.4762 Stainless Steel

Both AISI 309S stainless steel and EN 1.4762 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 86% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AISI 309S stainless steel and the bottom bar is EN 1.4762 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
190
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 42
13
Fatigue Strength, MPa 210
180
Poisson's Ratio 0.27
0.27
Shear Modulus, GPa 78
78
Shear Strength, MPa 400
370
Tensile Strength: Ultimate (UTS), MPa 580
620
Tensile Strength: Yield (Proof), MPa 230
310

Thermal Properties

Latent Heat of Fusion, J/g 290
300
Maximum Temperature: Corrosion, °C 440
440
Maximum Temperature: Mechanical, °C 1080
1150
Melting Completion (Liquidus), °C 1420
1410
Melting Onset (Solidus), °C 1370
1370
Specific Heat Capacity, J/kg-K 480
490
Thermal Conductivity, W/m-K 15
17
Thermal Expansion, µm/m-K 16
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
1.6
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 19
12
Density, g/cm3 7.8
7.6
Embodied Carbon, kg CO2/kg material 3.6
2.5
Embodied Energy, MJ/kg 51
37
Embodied Water, L/kg 170
170

Common Calculations

PREN (Pitting Resistance) 23
25
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
67
Resilience: Unit (Modulus of Resilience), kJ/m3 140
250
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
26
Strength to Weight: Axial, points 21
23
Strength to Weight: Bending, points 20
21
Thermal Diffusivity, mm2/s 4.0
4.6
Thermal Shock Resistance, points 13
22

Alloy Composition

Aluminum (Al), % 0
1.2 to 1.7
Carbon (C), % 0 to 0.080
0 to 0.12
Chromium (Cr), % 22 to 24
23 to 26
Iron (Fe), % 58.1 to 66
69.7 to 75.1
Manganese (Mn), % 0 to 2.0
0 to 1.0
Nickel (Ni), % 12 to 15
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 0.75
0.7 to 1.4
Sulfur (S), % 0 to 0.030
0 to 0.015