AISI 310 Stainless Steel vs. 3203 Aluminum

AISI 310 stainless steel belongs to the iron alloys classification, while 3203 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AISI 310 stainless steel and the bottom bar is 3203 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
70
Elongation at Break, % 34 to 45
4.5 to 29
Fatigue Strength, MPa 240 to 280
46 to 92
Poisson's Ratio 0.27
0.33
Shear Modulus, GPa 78
26
Shear Strength, MPa 420 to 470
72 to 120
Tensile Strength: Ultimate (UTS), MPa 600 to 710
110 to 200
Tensile Strength: Yield (Proof), MPa 260 to 350
39 to 190

Thermal Properties

Latent Heat of Fusion, J/g 310
400
Maximum Temperature: Mechanical, °C 1040
180
Melting Completion (Liquidus), °C 1450
650
Melting Onset (Solidus), °C 1400
620
Specific Heat Capacity, J/kg-K 480
900
Thermal Conductivity, W/m-K 15
170
Thermal Expansion, µm/m-K 15
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
43
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
140

Otherwise Unclassified Properties

Base Metal Price, % relative 25
9.0
Density, g/cm3 7.8
2.8
Embodied Carbon, kg CO2/kg material 4.3
8.1
Embodied Energy, MJ/kg 61
150
Embodied Water, L/kg 190
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 200 to 220
8.0 to 25
Resilience: Unit (Modulus of Resilience), kJ/m3 170 to 310
11 to 250
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
50
Strength to Weight: Axial, points 21 to 25
11 to 20
Strength to Weight: Bending, points 20 to 22
19 to 28
Thermal Diffusivity, mm2/s 3.9
70
Thermal Shock Resistance, points 14 to 17
4.9 to 8.8

Alloy Composition

Aluminum (Al), % 0
96.9 to 99
Carbon (C), % 0 to 0.25
0
Chromium (Cr), % 24 to 26
0
Copper (Cu), % 0
0 to 0.050
Iron (Fe), % 48.2 to 57
0 to 0.7
Manganese (Mn), % 0 to 2.0
1.0 to 1.5
Nickel (Ni), % 19 to 22
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 1.5
0 to 0.6
Sulfur (S), % 0 to 0.030
0
Zinc (Zn), % 0
0 to 0.1
Residuals, % 0
0 to 0.15