AISI 310 Stainless Steel vs. ASTM A229 Spring Steel
Both AISI 310 stainless steel and ASTM A229 spring steel are iron alloys. They have 54% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is AISI 310 stainless steel and the bottom bar is ASTM A229 spring steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 180 to 220 | |
| 490 to 550 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 34 to 45 | |
| 14 |
| Fatigue Strength, MPa | 240 to 280 | |
| 710 to 790 |
| Poisson's Ratio | 0.27 | |
| 0.29 |
| Shear Modulus, GPa | 78 | |
| 72 |
| Shear Strength, MPa | 420 to 470 | |
| 1020 to 1140 |
| Tensile Strength: Ultimate (UTS), MPa | 600 to 710 | |
| 1690 to 1890 |
| Tensile Strength: Yield (Proof), MPa | 260 to 350 | |
| 1100 to 1230 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 1040 | |
| 400 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1450 |
| Melting Onset (Solidus), °C | 1400 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 15 | |
| 50 |
| Thermal Expansion, µm/m-K | 15 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.5 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 25 | |
| 1.8 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 4.3 | |
| 1.4 |
| Embodied Energy, MJ/kg | 61 | |
| 19 |
| Embodied Water, L/kg | 190 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 200 to 220 | |
| 200 to 230 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 170 to 310 | |
| 3260 to 4080 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 21 to 25 | |
| 60 to 67 |
| Strength to Weight: Bending, points | 20 to 22 | |
| 40 to 43 |
| Thermal Diffusivity, mm2/s | 3.9 | |
| 14 |
| Thermal Shock Resistance, points | 14 to 17 | |
| 54 to 60 |
Alloy Composition
| Carbon (C), % | 0 to 0.25 | |
| 0.55 to 0.85 |
| Chromium (Cr), % | 24 to 26 | |
| 0 |
| Iron (Fe), % | 48.2 to 57 | |
| 97.5 to 99 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0.3 to 1.2 |
| Nickel (Ni), % | 19 to 22 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.5 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.050 |