AISI 310H Stainless Steel vs. 50Cr-50Ni-Cb Alloy

AISI 310H stainless steel belongs to the iron alloys classification, while 50Cr-50Ni-Cb alloy belongs to the otherwise unclassified metals. They have 46% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is AISI 310H stainless steel and the bottom bar is 50Cr-50Ni-Cb alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 40
5.6
Poisson's Ratio 0.27
0.26
Shear Modulus, GPa 79
84
Tensile Strength: Ultimate (UTS), MPa 580
620
Tensile Strength: Yield (Proof), MPa 230
390

Thermal Properties

Latent Heat of Fusion, J/g 300
350
Specific Heat Capacity, J/kg-K 480
480
Thermal Expansion, µm/m-K 16
15

Otherwise Unclassified Properties

Base Metal Price, % relative 25
60
Density, g/cm3 7.9
8.0
Embodied Carbon, kg CO2/kg material 4.3
9.2
Embodied Energy, MJ/kg 61
130
Embodied Water, L/kg 190
350

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
30
Resilience: Unit (Modulus of Resilience), kJ/m3 130
370
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
21
Strength to Weight: Bending, points 20
20
Thermal Shock Resistance, points 13
14

Alloy Composition

Aluminum (Al), % 0
0 to 0.25
Carbon (C), % 0.040 to 0.1
0 to 0.1
Chromium (Cr), % 24 to 26
47 to 52
Iron (Fe), % 49.1 to 57
0 to 1.0
Manganese (Mn), % 0 to 2.0
0 to 0.3
Nickel (Ni), % 19 to 22
43.3 to 51.6
Niobium (Nb), % 0
1.4 to 1.7
Nitrogen (N), % 0
0 to 0.16
Phosphorus (P), % 0 to 0.045
0 to 0.020
Silicon (Si), % 0 to 0.75
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.020
Titanium (Ti), % 0
0 to 0.5