AISI 310H Stainless Steel vs. AWS E110C-K3

Both AISI 310H stainless steel and AWS E110C-K3 are iron alloys. They have 56% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AISI 310H stainless steel and the bottom bar is AWS E110C-K3.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 40
17
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 79
73
Tensile Strength: Ultimate (UTS), MPa 580
870
Tensile Strength: Yield (Proof), MPa 230
760

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1360
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
48
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
9.0

Otherwise Unclassified Properties

Base Metal Price, % relative 25
3.4
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.3
1.7
Embodied Energy, MJ/kg 61
23
Embodied Water, L/kg 190
53

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
140
Resilience: Unit (Modulus of Resilience), kJ/m3 130
1550
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
31
Strength to Weight: Bending, points 20
26
Thermal Diffusivity, mm2/s 3.9
13
Thermal Shock Resistance, points 13
26

Alloy Composition

Carbon (C), % 0.040 to 0.1
0 to 0.15
Chromium (Cr), % 24 to 26
0 to 0.15
Copper (Cu), % 0
0 to 0.35
Iron (Fe), % 49.1 to 57
92.6 to 98.5
Manganese (Mn), % 0 to 2.0
0.75 to 2.3
Molybdenum (Mo), % 0
0.25 to 0.65
Nickel (Ni), % 19 to 22
0.5 to 2.5
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 0.75
0 to 0.8
Sulfur (S), % 0 to 0.030
0 to 0.025
Vanadium (V), % 0
0 to 0.030
Residuals, % 0
0 to 0.5