AISI 310H Stainless Steel vs. EN 1.4837 Stainless Steel
Both AISI 310H stainless steel and EN 1.4837 stainless steel are iron alloys. They have a moderately high 92% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is AISI 310H stainless steel and the bottom bar is EN 1.4837 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 | |
| 150 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Elongation at Break, % | 40 | |
| 6.8 |
| Fatigue Strength, MPa | 200 | |
| 120 |
| Poisson's Ratio | 0.27 | |
| 0.27 |
| Shear Modulus, GPa | 79 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 580 | |
| 500 |
| Tensile Strength: Yield (Proof), MPa | 230 | |
| 250 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 320 |
| Maximum Temperature: Corrosion, °C | 450 | |
| 440 |
| Maximum Temperature: Mechanical, °C | 1100 | |
| 1050 |
| Melting Completion (Liquidus), °C | 1410 | |
| 1390 |
| Melting Onset (Solidus), °C | 1360 | |
| 1350 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 490 |
| Thermal Conductivity, W/m-K | 15 | |
| 14 |
| Thermal Expansion, µm/m-K | 16 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.1 | |
| 2.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
| 2.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 25 | |
| 20 |
| Density, g/cm3 | 7.9 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 4.3 | |
| 3.7 |
| Embodied Energy, MJ/kg | 61 | |
| 53 |
| Embodied Water, L/kg | 190 | |
| 180 |
Common Calculations
| PREN (Pitting Resistance) | 25 | |
| 26 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 190 | |
| 29 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 | |
| 160 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 21 | |
| 18 |
| Strength to Weight: Bending, points | 20 | |
| 18 |
| Thermal Diffusivity, mm2/s | 3.9 | |
| 3.7 |
| Thermal Shock Resistance, points | 13 | |
| 11 |
Alloy Composition
| Carbon (C), % | 0.040 to 0.1 | |
| 0.3 to 0.5 |
| Chromium (Cr), % | 24 to 26 | |
| 24 to 27 |
| Iron (Fe), % | 49.1 to 57 | |
| 53.4 to 63.7 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 19 to 22 | |
| 11 to 14 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.75 | |
| 1.0 to 2.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |