AISI 310H Stainless Steel vs. N08026 Nickel

AISI 310H stainless steel belongs to the iron alloys classification, while N08026 nickel belongs to the nickel alloys. They have 76% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AISI 310H stainless steel and the bottom bar is N08026 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 40
34
Fatigue Strength, MPa 200
200
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 79
80
Shear Strength, MPa 400
410
Tensile Strength: Ultimate (UTS), MPa 580
620
Tensile Strength: Yield (Proof), MPa 230
270

Thermal Properties

Latent Heat of Fusion, J/g 300
310
Maximum Temperature: Mechanical, °C 1100
990
Melting Completion (Liquidus), °C 1410
1430
Melting Onset (Solidus), °C 1360
1380
Specific Heat Capacity, J/kg-K 480
460
Thermal Conductivity, W/m-K 15
12
Thermal Expansion, µm/m-K 16
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
1.6
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
1.7

Otherwise Unclassified Properties

Base Metal Price, % relative 25
41
Density, g/cm3 7.9
8.2
Embodied Carbon, kg CO2/kg material 4.3
7.2
Embodied Energy, MJ/kg 61
98
Embodied Water, L/kg 190
240

Common Calculations

PREN (Pitting Resistance) 25
45
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
170
Resilience: Unit (Modulus of Resilience), kJ/m3 130
180
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
21
Strength to Weight: Bending, points 20
20
Thermal Diffusivity, mm2/s 3.9
3.2
Thermal Shock Resistance, points 13
15

Alloy Composition

Carbon (C), % 0.040 to 0.1
0 to 0.030
Chromium (Cr), % 24 to 26
22 to 26
Copper (Cu), % 0
2.0 to 4.0
Iron (Fe), % 49.1 to 57
24.4 to 37.9
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0
5.0 to 6.7
Nickel (Ni), % 19 to 22
33 to 37.2
Nitrogen (N), % 0
0.1 to 0.16
Phosphorus (P), % 0 to 0.045
0 to 0.030
Silicon (Si), % 0 to 0.75
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.030