AISI 310H Stainless Steel vs. R60706 Alloy

AISI 310H stainless steel belongs to the iron alloys classification, while R60706 alloy belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is AISI 310H stainless steel and the bottom bar is R60706 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
98
Elongation at Break, % 40
16
Poisson's Ratio 0.27
0.34
Shear Modulus, GPa 79
37
Tensile Strength: Ultimate (UTS), MPa 580
580
Tensile Strength: Yield (Proof), MPa 230
390

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Specific Heat Capacity, J/kg-K 480
270
Thermal Conductivity, W/m-K 15
17
Thermal Expansion, µm/m-K 16
6.3

Otherwise Unclassified Properties

Density, g/cm3 7.9
6.7
Embodied Water, L/kg 190
450

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
82
Resilience: Unit (Modulus of Resilience), kJ/m3 130
760
Stiffness to Weight: Axial, points 14
8.1
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 21
24
Strength to Weight: Bending, points 20
23
Thermal Diffusivity, mm2/s 3.9
9.5
Thermal Shock Resistance, points 13
67

Alloy Composition

Carbon (C), % 0.040 to 0.1
0 to 0.050
Chromium (Cr), % 24 to 26
0 to 0.2
Hafnium (Hf), % 0
0 to 4.5
Hydrogen (H), % 0
0 to 0.0050
Iron (Fe), % 49.1 to 57
0 to 0.2
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 19 to 22
0
Niobium (Nb), % 0
2.0 to 3.0
Nitrogen (N), % 0
0 to 0.025
Oxygen (O), % 0
0 to 0.16
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 0.75
0
Sulfur (S), % 0 to 0.030
0
Zirconium (Zr), % 0
91 to 98