AISI 310H Stainless Steel vs. S41041 Stainless Steel

Both AISI 310H stainless steel and S41041 stainless steel are iron alloys. They have 66% of their average alloy composition in common. There are 34 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AISI 310H stainless steel and the bottom bar is S41041 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
240
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 40
17
Fatigue Strength, MPa 200
350
Poisson's Ratio 0.27
0.28
Reduction in Area, % 51
56
Shear Modulus, GPa 79
76
Shear Strength, MPa 400
560
Tensile Strength: Ultimate (UTS), MPa 580
910
Tensile Strength: Yield (Proof), MPa 230
580

Thermal Properties

Latent Heat of Fusion, J/g 300
270
Maximum Temperature: Corrosion, °C 450
430
Maximum Temperature: Mechanical, °C 1100
740
Melting Completion (Liquidus), °C 1410
1450
Melting Onset (Solidus), °C 1360
1410
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
29
Thermal Expansion, µm/m-K 16
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 25
8.5
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.3
2.2
Embodied Energy, MJ/kg 61
31
Embodied Water, L/kg 190
100

Common Calculations

PREN (Pitting Resistance) 25
13
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
140
Resilience: Unit (Modulus of Resilience), kJ/m3 130
860
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
32
Strength to Weight: Bending, points 20
27
Thermal Diffusivity, mm2/s 3.9
7.8
Thermal Shock Resistance, points 13
33

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0.040 to 0.1
0.13 to 0.18
Chromium (Cr), % 24 to 26
11.5 to 13
Iron (Fe), % 49.1 to 57
84.5 to 87.8
Manganese (Mn), % 0 to 2.0
0.4 to 0.6
Molybdenum (Mo), % 0
0 to 0.2
Nickel (Ni), % 19 to 22
0 to 0.5
Niobium (Nb), % 0
0.15 to 0.45
Phosphorus (P), % 0 to 0.045
0 to 0.030
Silicon (Si), % 0 to 0.75
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.030