AISI 310MoLN Stainless Steel vs. ACI-ASTM CF3 Steel

Both AISI 310MoLN stainless steel and ACI-ASTM CF3 steel are iron alloys. They have 80% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AISI 310MoLN stainless steel and the bottom bar is ACI-ASTM CF3 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
140
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 28
60
Fatigue Strength, MPa 210
270
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
77
Tensile Strength: Ultimate (UTS), MPa 610
510
Tensile Strength: Yield (Proof), MPa 290
250

Thermal Properties

Latent Heat of Fusion, J/g 300
300
Maximum Temperature: Corrosion, °C 450
420
Maximum Temperature: Mechanical, °C 1100
960
Melting Completion (Liquidus), °C 1420
1420
Melting Onset (Solidus), °C 1380
1450
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 14
16
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 28
16
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 5.0
3.2
Embodied Energy, MJ/kg 70
45
Embodied Water, L/kg 200
150

Common Calculations

PREN (Pitting Resistance) 34
20
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
250
Resilience: Unit (Modulus of Resilience), kJ/m3 200
160
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
18
Strength to Weight: Bending, points 20
18
Thermal Diffusivity, mm2/s 3.7
4.3
Thermal Shock Resistance, points 14
11

Alloy Composition

Carbon (C), % 0 to 0.020
0 to 0.030
Chromium (Cr), % 24 to 26
17 to 21
Iron (Fe), % 45.2 to 53.8
62.9 to 75
Manganese (Mn), % 0 to 2.0
0 to 1.5
Molybdenum (Mo), % 1.6 to 2.6
0 to 0.5
Nickel (Ni), % 20.5 to 23.5
8.0 to 12
Nitrogen (N), % 0.090 to 0.15
0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 2.0
Sulfur (S), % 0 to 0.010
0 to 0.040