AISI 310MoLN Stainless Steel vs. AISI 304N Stainless Steel

Both AISI 310MoLN stainless steel and AISI 304N stainless steel are iron alloys. They have 79% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AISI 310MoLN stainless steel and the bottom bar is AISI 304N stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
190 to 360
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 28
9.1 to 45
Fatigue Strength, MPa 210
220 to 440
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
77
Shear Strength, MPa 400
420 to 700
Tensile Strength: Ultimate (UTS), MPa 610
620 to 1180
Tensile Strength: Yield (Proof), MPa 290
270 to 850

Thermal Properties

Latent Heat of Fusion, J/g 300
290
Maximum Temperature: Corrosion, °C 450
420
Maximum Temperature: Mechanical, °C 1100
960
Melting Completion (Liquidus), °C 1420
1420
Melting Onset (Solidus), °C 1380
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 14
16
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 28
15
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 5.0
3.0
Embodied Energy, MJ/kg 70
43
Embodied Water, L/kg 200
150

Common Calculations

PREN (Pitting Resistance) 34
21
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
98 to 280
Resilience: Unit (Modulus of Resilience), kJ/m3 200
180 to 1830
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
22 to 42
Strength to Weight: Bending, points 20
21 to 32
Thermal Diffusivity, mm2/s 3.7
4.2
Thermal Shock Resistance, points 14
14 to 26

Alloy Composition

Carbon (C), % 0 to 0.020
0 to 0.080
Chromium (Cr), % 24 to 26
18 to 20
Iron (Fe), % 45.2 to 53.8
66.4 to 73.9
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 1.6 to 2.6
0
Nickel (Ni), % 20.5 to 23.5
8.0 to 10.5
Nitrogen (N), % 0.090 to 0.15
0.1 to 0.16
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0 to 0.5
0 to 0.75
Sulfur (S), % 0 to 0.010
0 to 0.030