AISI 310S Stainless Steel vs. CR011A Copper

AISI 310S stainless steel belongs to the iron alloys classification, while CR011A copper belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AISI 310S stainless steel and the bottom bar is CR011A copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
120
Elongation at Break, % 34 to 44
15
Poisson's Ratio 0.27
0.34
Shear Modulus, GPa 79
43
Tensile Strength: Ultimate (UTS), MPa 600 to 710
220
Tensile Strength: Yield (Proof), MPa 270 to 350
130

Thermal Properties

Latent Heat of Fusion, J/g 310
210
Maximum Temperature: Mechanical, °C 1100
200
Melting Completion (Liquidus), °C 1450
1090
Melting Onset (Solidus), °C 1400
1040
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 16
390
Thermal Expansion, µm/m-K 16
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
100
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
100

Otherwise Unclassified Properties

Base Metal Price, % relative 25
32
Density, g/cm3 7.9
9.0
Embodied Carbon, kg CO2/kg material 4.3
2.6
Embodied Energy, MJ/kg 61
42
Embodied Water, L/kg 190
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 200 to 220
29
Resilience: Unit (Modulus of Resilience), kJ/m3 190 to 310
76
Stiffness to Weight: Axial, points 14
7.2
Stiffness to Weight: Bending, points 25
18
Strength to Weight: Axial, points 21 to 25
6.8
Strength to Weight: Bending, points 20 to 22
9.0
Thermal Diffusivity, mm2/s 4.1
110
Thermal Shock Resistance, points 14 to 16
7.8

Alloy Composition

Bismuth (Bi), % 0
0 to 0.00050
Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 24 to 26
0
Copper (Cu), % 0
99.88 to 99.97
Iron (Fe), % 48.3 to 57
0
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 19 to 22
0
Oxygen (O), % 0
0 to 0.040
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 1.5
0
Silver (Ag), % 0
0.030 to 0.050
Sulfur (S), % 0 to 0.030
0