AISI 312 Stainless Steel vs. ASTM Grade LC2 Steel

Both AISI 312 stainless steel and ASTM grade LC2 steel are iron alloys. They have 69% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AISI 312 stainless steel and the bottom bar is ASTM grade LC2 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 250
170
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 28
27
Fatigue Strength, MPa 370
230
Poisson's Ratio 0.27
0.29
Reduction in Area, % 56
40
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 780
570
Tensile Strength: Yield (Proof), MPa 510
310

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
410
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
52
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 17
3.4
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 3.4
1.6
Embodied Energy, MJ/kg 48
22
Embodied Water, L/kg 170
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
130
Resilience: Unit (Modulus of Resilience), kJ/m3 640
260
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 28
20
Strength to Weight: Bending, points 24
19
Thermal Diffusivity, mm2/s 4.3
14
Thermal Shock Resistance, points 21
17

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.25
Chromium (Cr), % 24 to 26
0
Iron (Fe), % 62.2 to 69.2
95.3 to 97.5
Manganese (Mn), % 0 to 2.0
0.5 to 0.8
Molybdenum (Mo), % 1.2 to 2.0
0
Nickel (Ni), % 5.5 to 6.5
2.0 to 3.0
Nitrogen (N), % 0.14 to 0.2
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.045