AISI 316 Stainless Steel vs. EN 1.4595 Stainless Steel

Both AISI 316 stainless steel and EN 1.4595 stainless steel are iron alloys. They have 83% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AISI 316 stainless steel and the bottom bar is EN 1.4595 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 8.0 to 55
29
Fatigue Strength, MPa 210 to 430
180
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
76
Shear Strength, MPa 350 to 690
310
Tensile Strength: Ultimate (UTS), MPa 520 to 1180
470
Tensile Strength: Yield (Proof), MPa 230 to 850
250

Thermal Properties

Latent Heat of Fusion, J/g 290
280
Maximum Temperature: Corrosion, °C 410
460
Maximum Temperature: Mechanical, °C 590
810
Melting Completion (Liquidus), °C 1400
1450
Melting Onset (Solidus), °C 1380
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 15
30
Thermal Expansion, µm/m-K 16
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 19
10
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 3.9
2.4
Embodied Energy, MJ/kg 53
34
Embodied Water, L/kg 150
110

Common Calculations

PREN (Pitting Resistance) 26
15
Resilience: Ultimate (Unit Rupture Work), MJ/m3 85 to 260
110
Resilience: Unit (Modulus of Resilience), kJ/m3 130 to 1820
150
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 18 to 41
17
Strength to Weight: Bending, points 18 to 31
17
Thermal Diffusivity, mm2/s 4.1
8.1
Thermal Shock Resistance, points 11 to 26
17

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.020
Chromium (Cr), % 16 to 18
14 to 16
Iron (Fe), % 62 to 72
81.3 to 85.8
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 2.0 to 3.0
0
Nickel (Ni), % 10 to 14
0
Niobium (Nb), % 0
0.2 to 0.6
Nitrogen (N), % 0 to 0.1
0 to 0.020
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 0.75
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015