AISI 316 Stainless Steel vs. SAE-AISI M36 Steel
Both AISI 316 stainless steel and SAE-AISI M36 steel are iron alloys. They have 74% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is AISI 316 stainless steel and the bottom bar is SAE-AISI M36 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 200 | |
200 |
Poisson's Ratio | 0.28 | |
0.29 |
Shear Modulus, GPa | 78 | |
78 |
Tensile Strength: Ultimate (UTS), MPa | 520 to 1180 | |
810 to 2190 |
Thermal Properties
Latent Heat of Fusion, J/g | 290 | |
260 |
Melting Completion (Liquidus), °C | 1400 | |
1600 |
Melting Onset (Solidus), °C | 1380 | |
1550 |
Specific Heat Capacity, J/kg-K | 470 | |
440 |
Thermal Conductivity, W/m-K | 15 | |
19 |
Thermal Expansion, µm/m-K | 16 | |
12 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 19 | |
38 |
Density, g/cm3 | 7.9 | |
8.4 |
Embodied Carbon, kg CO2/kg material | 3.9 | |
9.5 |
Embodied Energy, MJ/kg | 53 | |
140 |
Embodied Water, L/kg | 150 | |
140 |
Common Calculations
PREN (Pitting Resistance) | 26 | |
31 |
Stiffness to Weight: Axial, points | 14 | |
13 |
Stiffness to Weight: Bending, points | 25 | |
23 |
Strength to Weight: Axial, points | 18 to 41 | |
27 to 72 |
Strength to Weight: Bending, points | 18 to 31 | |
23 to 44 |
Thermal Diffusivity, mm2/s | 4.1 | |
5.1 |
Thermal Shock Resistance, points | 11 to 26 | |
25 to 68 |
Alloy Composition
Carbon (C), % | 0 to 0.080 | |
0.8 to 0.9 |
Chromium (Cr), % | 16 to 18 | |
3.8 to 4.5 |
Cobalt (Co), % | 0 | |
7.8 to 8.8 |
Copper (Cu), % | 0 | |
0 to 0.25 |
Iron (Fe), % | 62 to 72 | |
70.1 to 75.5 |
Manganese (Mn), % | 0 to 2.0 | |
0.15 to 0.4 |
Molybdenum (Mo), % | 2.0 to 3.0 | |
4.6 to 5.5 |
Nickel (Ni), % | 10 to 14 | |
0 to 0.3 |
Nitrogen (N), % | 0 to 0.1 | |
0 |
Phosphorus (P), % | 0 to 0.045 | |
0 to 0.030 |
Silicon (Si), % | 0 to 0.75 | |
0.2 to 0.45 |
Sulfur (S), % | 0 to 0.030 | |
0 to 0.030 |
Tungsten (W), % | 0 | |
5.5 to 6.5 |
Vanadium (V), % | 0 | |
1.8 to 2.3 |