AISI 316L Stainless Steel vs. EN 1.4310 Stainless Steel

Both AISI 316L stainless steel and EN 1.4310 stainless steel are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AISI 316L stainless steel and the bottom bar is EN 1.4310 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170 to 350
200 to 270
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 9.0 to 50
14 to 45
Fatigue Strength, MPa 170 to 450
240 to 330
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
77
Shear Strength, MPa 370 to 690
510 to 550
Tensile Strength: Ultimate (UTS), MPa 530 to 1160
730 to 900
Tensile Strength: Yield (Proof), MPa 190 to 870
260 to 570

Thermal Properties

Latent Heat of Fusion, J/g 290
290
Maximum Temperature: Corrosion, °C 410
410
Maximum Temperature: Mechanical, °C 870
910
Melting Completion (Liquidus), °C 1400
1420
Melting Onset (Solidus), °C 1380
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 16
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 19
14
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 3.9
2.9
Embodied Energy, MJ/kg 53
42
Embodied Water, L/kg 150
140

Common Calculations

PREN (Pitting Resistance) 26
20
Resilience: Ultimate (Unit Rupture Work), MJ/m3 77 to 230
110 to 260
Resilience: Unit (Modulus of Resilience), kJ/m3 93 to 1880
170 to 830
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 19 to 41
26 to 32
Strength to Weight: Bending, points 18 to 31
23 to 27
Thermal Diffusivity, mm2/s 4.1
4.0
Thermal Shock Resistance, points 12 to 25
15 to 18

Alloy Composition

Carbon (C), % 0 to 0.030
0.050 to 0.15
Chromium (Cr), % 16 to 18
16 to 19
Iron (Fe), % 62 to 72
66.4 to 78
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 2.0 to 3.0
0 to 0.8
Nickel (Ni), % 10 to 14
6.0 to 9.5
Nitrogen (N), % 0 to 0.1
0 to 0.1
Phosphorus (P), % 0 to 0.045
0 to 0.045
Silicon (Si), % 0 to 0.75
0 to 2.0
Sulfur (S), % 0 to 0.030
0 to 0.015

Comparable Variants