AISI 316L Stainless Steel vs. EN 1.4567 Stainless Steel
Both AISI 316L stainless steel and EN 1.4567 stainless steel are iron alloys. They have a moderately high 95% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is AISI 316L stainless steel and the bottom bar is EN 1.4567 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 170 to 350 | |
190 to 240 |
Elastic (Young's, Tensile) Modulus, GPa | 200 | |
190 |
Elongation at Break, % | 9.0 to 50 | |
22 to 51 |
Fatigue Strength, MPa | 170 to 450 | |
190 to 260 |
Poisson's Ratio | 0.28 | |
0.28 |
Shear Modulus, GPa | 78 | |
76 |
Shear Strength, MPa | 370 to 690 | |
390 to 490 |
Tensile Strength: Ultimate (UTS), MPa | 530 to 1160 | |
550 to 780 |
Tensile Strength: Yield (Proof), MPa | 190 to 870 | |
200 to 390 |
Thermal Properties
Latent Heat of Fusion, J/g | 290 | |
290 |
Maximum Temperature: Corrosion, °C | 410 | |
420 |
Maximum Temperature: Mechanical, °C | 870 | |
930 |
Melting Completion (Liquidus), °C | 1400 | |
1410 |
Melting Onset (Solidus), °C | 1380 | |
1370 |
Specific Heat Capacity, J/kg-K | 470 | |
480 |
Thermal Conductivity, W/m-K | 15 | |
11 |
Thermal Expansion, µm/m-K | 16 | |
17 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 2.3 | |
2.4 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 2.6 | |
2.7 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 19 | |
16 |
Density, g/cm3 | 7.9 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 3.9 | |
3.1 |
Embodied Energy, MJ/kg | 53 | |
43 |
Embodied Water, L/kg | 150 | |
150 |
Common Calculations
PREN (Pitting Resistance) | 26 | |
19 |
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 77 to 230 | |
150 to 220 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 93 to 1880 | |
100 to 400 |
Stiffness to Weight: Axial, points | 14 | |
14 |
Stiffness to Weight: Bending, points | 25 | |
25 |
Strength to Weight: Axial, points | 19 to 41 | |
19 to 27 |
Strength to Weight: Bending, points | 18 to 31 | |
19 to 24 |
Thermal Diffusivity, mm2/s | 4.1 | |
3.0 |
Thermal Shock Resistance, points | 12 to 25 | |
12 to 17 |
Alloy Composition
Carbon (C), % | 0 to 0.030 | |
0 to 0.040 |
Chromium (Cr), % | 16 to 18 | |
17 to 19 |
Copper (Cu), % | 0 | |
3.0 to 4.0 |
Iron (Fe), % | 62 to 72 | |
63.3 to 71.5 |
Manganese (Mn), % | 0 to 2.0 | |
0 to 2.0 |
Molybdenum (Mo), % | 2.0 to 3.0 | |
0 |
Nickel (Ni), % | 10 to 14 | |
8.5 to 10.5 |
Nitrogen (N), % | 0 to 0.1 | |
0 to 0.1 |
Phosphorus (P), % | 0 to 0.045 | |
0 to 0.045 |
Silicon (Si), % | 0 to 0.75 | |
0 to 1.0 |
Sulfur (S), % | 0 to 0.030 | |
0 to 0.015 |