AISI 316L Stainless Steel vs. Grade CW6M Nickel
AISI 316L stainless steel belongs to the iron alloys classification, while grade CW6M nickel belongs to the nickel alloys. They have a modest 34% of their average alloy composition in common, which, by itself, doesn't mean much. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is AISI 316L stainless steel and the bottom bar is grade CW6M nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 220 |
| Elongation at Break, % | 9.0 to 50 | |
| 29 |
| Fatigue Strength, MPa | 170 to 450 | |
| 210 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 78 | |
| 84 |
| Tensile Strength: Ultimate (UTS), MPa | 530 to 1160 | |
| 560 |
| Tensile Strength: Yield (Proof), MPa | 190 to 870 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 330 |
| Maximum Temperature: Mechanical, °C | 870 | |
| 970 |
| Melting Completion (Liquidus), °C | 1400 | |
| 1530 |
| Melting Onset (Solidus), °C | 1380 | |
| 1470 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 430 |
| Thermal Expansion, µm/m-K | 16 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 19 | |
| 65 |
| Density, g/cm3 | 7.9 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 3.9 | |
| 13 |
| Embodied Energy, MJ/kg | 53 | |
| 170 |
| Embodied Water, L/kg | 150 | |
| 300 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 77 to 230 | |
| 140 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 93 to 1880 | |
| 220 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 19 to 41 | |
| 18 |
| Strength to Weight: Bending, points | 18 to 31 | |
| 17 |
| Thermal Shock Resistance, points | 12 to 25 | |
| 16 |
Alloy Composition
| Carbon (C), % | 0 to 0.030 | |
| 0 to 0.070 |
| Chromium (Cr), % | 16 to 18 | |
| 17 to 20 |
| Iron (Fe), % | 62 to 72 | |
| 0 to 3.0 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 2.0 to 3.0 | |
| 17 to 20 |
| Nickel (Ni), % | 10 to 14 | |
| 54.9 to 66 |
| Nitrogen (N), % | 0 to 0.1 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.75 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |