AISI 316Ti Stainless Steel vs. AISI 316Cb Stainless Steel

Both AISI 316Ti stainless steel and AISI 316Cb stainless steel are iron alloys. Both are furnished in the annealed condition. Their average alloy composition is basically identical. There are 35 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is AISI 316Ti stainless steel and the bottom bar is AISI 316Cb stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
190
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 41
34
Fatigue Strength, MPa 200
180
Poisson's Ratio 0.28
0.28
Reduction in Area, % 45
46
Rockwell B Hardness 84
82
Shear Modulus, GPa 82
78
Shear Strength, MPa 400
390
Tensile Strength: Ultimate (UTS), MPa 580
580
Tensile Strength: Yield (Proof), MPa 230
230

Thermal Properties

Latent Heat of Fusion, J/g 290
290
Maximum Temperature: Corrosion, °C 470
490
Maximum Temperature: Mechanical, °C 940
940
Melting Completion (Liquidus), °C 1450
1450
Melting Onset (Solidus), °C 1380
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 17
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 19
22
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 4.0
4.4
Embodied Energy, MJ/kg 55
61
Embodied Water, L/kg 150
150

Common Calculations

PREN (Pitting Resistance) 26
26
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
160
Resilience: Unit (Modulus of Resilience), kJ/m3 140
130
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
20
Strength to Weight: Bending, points 20
20
Thermal Diffusivity, mm2/s 4.0
4.1
Thermal Shock Resistance, points 13
13

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.080
Chromium (Cr), % 16 to 18
16 to 18
Iron (Fe), % 61.3 to 72
60.9 to 72
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 2.0 to 3.0
2.0 to 3.0
Nickel (Ni), % 10 to 14
10 to 14
Niobium (Nb), % 0
0 to 1.1
Nitrogen (N), % 0 to 0.1
0 to 0.1
Phosphorus (P), % 0 to 0.045
0 to 0.045
Silicon (Si), % 0 to 0.75
0 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.030
Titanium (Ti), % 0 to 0.7
0