AISI 316Ti Stainless Steel vs. C86100 Bronze

AISI 316Ti stainless steel belongs to the iron alloys classification, while C86100 bronze belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AISI 316Ti stainless steel and the bottom bar is C86100 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 41
20
Poisson's Ratio 0.28
0.32
Shear Modulus, GPa 82
43
Tensile Strength: Ultimate (UTS), MPa 580
660
Tensile Strength: Yield (Proof), MPa 230
350

Thermal Properties

Latent Heat of Fusion, J/g 290
200
Maximum Temperature: Mechanical, °C 940
170
Melting Completion (Liquidus), °C 1450
940
Melting Onset (Solidus), °C 1380
900
Specific Heat Capacity, J/kg-K 470
420
Thermal Conductivity, W/m-K 15
35
Thermal Expansion, µm/m-K 17
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
8.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
9.0

Otherwise Unclassified Properties

Base Metal Price, % relative 19
24
Density, g/cm3 7.9
8.0
Embodied Carbon, kg CO2/kg material 4.0
2.9
Embodied Energy, MJ/kg 55
49
Embodied Water, L/kg 150
350

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
110
Resilience: Unit (Modulus of Resilience), kJ/m3 140
530
Stiffness to Weight: Axial, points 14
7.8
Stiffness to Weight: Bending, points 25
20
Strength to Weight: Axial, points 20
23
Strength to Weight: Bending, points 20
21
Thermal Diffusivity, mm2/s 4.0
10
Thermal Shock Resistance, points 13
21

Alloy Composition

Aluminum (Al), % 0
4.5 to 5.5
Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 16 to 18
0
Copper (Cu), % 0
66 to 68
Iron (Fe), % 61.3 to 72
2.0 to 4.0
Lead (Pb), % 0
0 to 0.1
Manganese (Mn), % 0 to 2.0
2.5 to 5.0
Molybdenum (Mo), % 2.0 to 3.0
0
Nickel (Ni), % 10 to 14
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 0.75
0
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
0 to 0.1
Titanium (Ti), % 0 to 0.7
0
Zinc (Zn), % 0
17.3 to 25