AISI 316Ti Stainless Steel vs. S43932 Stainless Steel

Both AISI 316Ti stainless steel and S43932 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 85% of their average alloy composition in common. There are 34 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AISI 316Ti stainless steel and the bottom bar is S43932 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
160
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 41
25
Fatigue Strength, MPa 200
160
Poisson's Ratio 0.28
0.28
Rockwell B Hardness 84
78
Shear Modulus, GPa 82
77
Shear Strength, MPa 400
300
Tensile Strength: Ultimate (UTS), MPa 580
460
Tensile Strength: Yield (Proof), MPa 230
230

Thermal Properties

Latent Heat of Fusion, J/g 290
280
Maximum Temperature: Corrosion, °C 470
570
Maximum Temperature: Mechanical, °C 940
890
Melting Completion (Liquidus), °C 1450
1440
Melting Onset (Solidus), °C 1380
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 15
23
Thermal Expansion, µm/m-K 17
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
2.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
3.2

Otherwise Unclassified Properties

Base Metal Price, % relative 19
12
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 4.0
2.7
Embodied Energy, MJ/kg 55
40
Embodied Water, L/kg 150
120

Common Calculations

PREN (Pitting Resistance) 26
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
96
Resilience: Unit (Modulus of Resilience), kJ/m3 140
140
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
17
Strength to Weight: Bending, points 20
17
Thermal Diffusivity, mm2/s 4.0
6.3
Thermal Shock Resistance, points 13
16

Alloy Composition

Aluminum (Al), % 0
0 to 0.15
Carbon (C), % 0 to 0.080
0 to 0.030
Chromium (Cr), % 16 to 18
17 to 19
Iron (Fe), % 61.3 to 72
76.7 to 83
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 2.0 to 3.0
0
Nickel (Ni), % 10 to 14
0 to 0.5
Niobium (Nb), % 0
0.2 to 0.75
Nitrogen (N), % 0 to 0.1
0 to 0.030
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 0.75
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Titanium (Ti), % 0 to 0.7
0.2 to 0.75