AISI 317LM Stainless Steel vs. EN 1.4422 Stainless Steel

Both AISI 317LM stainless steel and EN 1.4422 stainless steel are iron alloys. They have 79% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AISI 317LM stainless steel and the bottom bar is EN 1.4422 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 46
17
Fatigue Strength, MPa 210
380
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
76
Shear Strength, MPa 410
520
Tensile Strength: Ultimate (UTS), MPa 590
850
Tensile Strength: Yield (Proof), MPa 230
630

Thermal Properties

Latent Heat of Fusion, J/g 300
270
Maximum Temperature: Corrosion, °C 420
390
Maximum Temperature: Mechanical, °C 300
760
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1410
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 14
16
Thermal Expansion, µm/m-K 16
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 24
11
Density, g/cm3 8.0
7.9
Embodied Carbon, kg CO2/kg material 4.8
2.7
Embodied Energy, MJ/kg 65
37
Embodied Water, L/kg 170
110

Common Calculations

PREN (Pitting Resistance) 35
17
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
130
Resilience: Unit (Modulus of Resilience), kJ/m3 130
1000
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
30
Strength to Weight: Bending, points 20
25
Thermal Diffusivity, mm2/s 3.8
4.3
Thermal Shock Resistance, points 13
31

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.020
Chromium (Cr), % 18 to 20
11 to 13
Copper (Cu), % 0
0.2 to 0.8
Iron (Fe), % 54.4 to 64.5
76.8 to 83.5
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 4.0 to 5.0
1.3 to 1.8
Nickel (Ni), % 13.5 to 17.5
4.0 to 5.0
Nitrogen (N), % 0 to 0.2
0 to 0.020
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 0.75
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.0030